English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Alumina-lanthana (La at 1, 3, or 5 wt%) supports were prepared by sol-gel from Al alkoxide sol where La(NO3)3 was added. Annealed (550 ◦C) xerogels were characterized by N2 physisorption, thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopyenergy dispersive spectroscopy (SEM-EDS), CO2-adsorption studied in IR region, Raman and ultraviolet-vis (UV-vis) spectroscopies. The texture of amorphous binary matrices of high La dispersion was adequate to applications in catalysts for middle distillates hydrodesulfurization (HDS). Generally, the amount and strength of surface basic sites increased with La content in solids. Mo (at 2.8 at. nm−2) and Co (at Co/(Co+Mo) = 0.3) were deposited over carriers by one-pot simultaneous impregnation in the presence of PO43− (P2O5/(NiO+MoO3) = 0.2 mass ratio). Calcined (400 ◦C) Co-Mo-P impregnated precursors had decreased basicity as to that of corresponding carriers, suggesting strong La-deposited species interaction. As La content in carriers increased Mo=O Raman stretching vibrations shifted to lower wave-numbers (949 to 935 cm−1) suggesting octahedral molybdates coordination change to tetrahedral. Although La at the lowest concentration (1 wt%) enhanced dibenzothiophene, HDS (~38% higher as to the Al2O3-supported formulation) desulfurization was significantly diminished at augmented content. Presence of hardly sulfidable tetrahedral Mo originated during impregnation at basic conditions in pores of La-modified carriers seemed to dictate observed behavior. Rare earth content in formulations enhanced selectivity to biphenyl.

Dibenzothiophene Hydrodesulfurization over P-CoMo on Sol-Gel Alumina Modified by La Addition. Effect of Rare-Earth Content