English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Regeneration process and adsorbent performance were investigated by a fixed-bed adsorber at 300 °C. Surface species, zeolite structure, and Pt morphology were characterized by FT-IR, XRPD and EXAFS, respectively. Performance test results indicated that ethanol adsorption capacity of Pt/NaY-SiO2 is about 2.5 times that of NaY-SiO2. After regeneration, adsorption-capacity loss is 2.5 and 43%, respectively, for Pt/NaY-SiO2 regenerated at superficial velocity of 13.2 (PtR(HF)) and 5.3 cm/min (PtR(LF)); in contrast, it is 8 and 21%, respectively, for NaYR(HF) and NaYR(LF). The appearance of absorption bands in the CH stretching region (υCH) of the IR spectra characterizing the regenerated NaY-SiO2 suggested that the adsorption-capacity loss for NaY-SiO2 was mainly caused by the deposition of carbonaceous species formed in regeneration, which cannot be burned off readily at 300 °C. In contrast, no υCH bands have been observed for the IR spectra of PtR(HF) and PtR(LF), indicating that Pt helps to burn off carbonaceous species. However, Pt agglomeration was observed in TEM and EXAFS for Pt/NaY-SiO2(LF). The appearance of a υCO band at about 2085 cm−1 of the IR spectra characterizing PtR(LF) suggested that Pt agglomeration was induced by CO adsorption. The growth of Pt particles decreases the ethanol adsorbed on Pt together with the conversion of ethanol to ethoxides and aldehyde, leading to a decrease of adsorption capacity.

Air Regeneration of Ethanol-Laden Pellet NaY-SiO2 and Pt/NaY-SiO2: Effects of Air Flow Rate on Pt Morphology and Regeneration Efficiency