English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Metastable ScxAl1-xN and YxAl1-xN thin films were deposited in an ultra high vacuum system using reactive magnetron sputter epitaxy from elemental Al, Sc, and Y targets in Ar/N2 gas mixture. Their structural, electrical, optical, mechanical, and piezoelectrical properties were investigated by using the transmission electron microscopy, x-ray diffraction, spectroscopic ellipsometry, I-V and C-V measurements, nanoindentation, and two different techniques for piezoelectric characterization: piezoresponse force microscopy and double beam interferometry. Compared to AlN, improved electromechanical coupling and increase in piezoelectric response was found in ScxAl1-xN/TiN/Al2O3 structures with Sc content up to x=0.2. Decreasing the growth temperature down to 400 °C improved the microstructure and crystalline quality of the material. Microstructure of the films had a stronger influence on piezoelectric properties than the crystalline quality, which affected the leakage currents. When x was increased from x=0 to x=0.3, the hardness and reduced Young’s modulus Er showed a decrease from 17 GPa to 11 GPa, and 265 GPa down to 224 GPa, respectively. In ScxAl1-xN/InyAl1-yN superlattices, ScxAl1-xN layers negative lattice mismatched to In-rich InyAl1-yN were found to be stable at higher Sc concentration (x=0.4) than lattice-matched or positive lattice mismatched layers, confirmed by first principle (ab initio) calculations using density-functional formalism. Al-rich YxAl1-xN thin films were synthesized and reported for the first time. Formation of solid solution was observed up to x=0.22 and an increase in growth temperature up to 900°C improved the crystalline quality of the YxAl1-xN films. The band gap of YxAl1-xN decreased from 6.2 eV for AlN down to 4.5 eV (x=0.22) and was shown to follow Vegard’s rule. Refractive indices and extinction coefficients were also determined. Lattice constants of wurtzite YxAl1-xN measured experimentally are in good agreement with theoretical predictions obtained through ab initio calculations. The mixing enthalp

Metastable ScAlN and YAlN Thin Films Grown by Reactive Magnetron Sputter Epitaxy