English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

This study focuses on the effect of crosslinking density on the mechanical response of polystyrene-co-divinylbenzene (PS-DVB) particles under compression by means of nanoindentation-based flat punch method combined with SEM observation of particle morphologies. The monodisperse PS-DVB particles with about 5 µm in diameter are produced by the Ugelstad activated swelling method and the crosslinking density defined as the weight percentage of activated crosslinker DVB during the preparation process varies from 2.0 to 55.3%. Results show that the particle stress–strain behaviour is independent of the crosslinking density if the strain is less than 10%. With increasing strain level over 10%, a higher crosslinking leads to a stiffer behaviour of the particles. While slightly crosslinked (2.0 and 5.0 wt%) particles undergo plastic deformation with crazing and residual strain, highly crosslinked (21.3, 32.0 and 55.3 wt%) counterparts experience perfectly viscoelastic deformation. The crosslinking density significantly influences the fracture property as well as the failure morphology. Slightly crosslinked particles become permanently deformed after compression, while highly crosslinked ones are entirely fragmented once a critical strain is reached

Crosslinking effect on the deformation and fracture of monodisperse polystyrene-co-divinylbenzene particles