English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

A drive shaft of a multifunctional mechanical processing machine for large components broke down during processing. The OEM shaft was worn-out after years of operation and was recently replaced. The replaced drive shaft was delivered to the materials laboratory of the Berlin gas turbine plant in order to identify the cause of the damage. It was found that the component failed due to high cycle fatigue failure, HCF, on the tooth roots after a short period of operation. The teeth of the damaged shaft were inappropriately induction surface hardened.

practical metallography

Metallurgical Failure Investigation of a Surface Hardened Drive Shaft Made of Tempered Low-Alloy Steel 25CrMo4 (1.7218): Dedicated to the Lette Verein Berlin on the occasion of its 150 th  jubilee