English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Two MgLiAl alloys consisting either of α (hcp) + β (bcc) phases or only β phase were subjected to twist channel angular pressing TCAP (with helical component) or cyclic compression to a total strain of  ∊  = 5 in order to study the effectiveness of various deformation modes on grain refinement. After the first TCAP pass grains of α phase were refined from 30 μm down to about 6 μm and of β phase from initial 200 μm down to 8 μm. MAXStrain cycling led to much finer grains of α and β phases in the range 200 – 300 nm causing higher hardening and indicating higher effectiveness of the process. The Li 2 MgAl precipitates were refined during severe plastic deformation (SPD) processes and in addition fine particles of hexagonal α phase of size below 100 nm were observed within the β phase showing orientation relationship (0001) α ‖ (011) β. Two-phase material after SPD showed deviation of about 1.5° from the ideal Burgers orientation relationship (0001) α ‖ (011) β.

Structure of MgLiAl alloys after various routes of severe plastic deformation studied by TEM