English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

The oxidation behaviour of experimental Co – Re-based alloy at 1000 °C was studied. A set of binary, ternary and quaternary alloys from the Co – Re – Cr – C system was used as model alloys to understand the role each alloying element plays on oxidation. The morphology and composition of the oxide scale that formed was analysed by X-ray diffraction, energy dispersive spectroscopy and scanning electron microscopy. It was found that the present Co – Re alloys with 23 at.% and 30 at.% Cr additions behaved very similarly to Co – Cr binary alloys with equivalent Cr content. The oxide scale was multilayered, consisting of a dense CoO outer layer, a porous mixed oxide layer containing Co-oxide and Co – Cr spinel, and a discontinuous and non-protective Cr 3 O 2  layer. The binary Co – Re alloy behaved differently in oxidation, and it formed only a monolithic CoO scale. However, Re in combination with Cr promotes Cr – Re-rich phase formation, which oxidises preferentially compared to the Co matrix. Carbon ties up part of the Cr to form Cr 23 C 6  type carbides. However, these carbides are not stable at 1000 °C and dissolved with time, therefore C had only a minor role in the oxidation behaviour. In general, increasing Cr content in the alloy improved oxidation resistance.

Oxidation behaviour of experimental Co–Re-base alloys in laboratory air at 1000°C