Open AccessStudies on Mild Steel Particulates Reinforced Duralumin Composite Fabricated Through Powder Metallurgy Route
Author(s) -
Y. M. Shivaprakash et al. Y. M. Shivaprakash et al.,
TJPRC
Publication year - 2019
Publication title -
international journal of mechanical and production engineering research and development
Language(s) - English
Resource type - Journals
eISSN - 2249-8001
pISSN - 2249-6890
DOI - 10.24247/ijmperdapr201988
Subject(s) - powder metallurgy , composite number , materials science , metallurgy , particulates , composite material , microstructure , chemistry , organic chemistry
In the present study Duralumin(DA) based Mild Steel particles (MSp-6% wt. and 12% wt.) reinforced composite are fabricated by cold compacting the milled powders. The mechanically mixed powders are compacted in a die cavity by applying a uniaxial steady load in the range 22-38 T. The hardness of green compacts produced are increased by sintering. The SEM images showed an even dispersion of MSp in the duralumin alloy and elemental composition is confirmed by the EDAX spectrum. The sintered specimens were further subjected to aging treatment. Compacts were soaked at 5500C for a span of 2 h and then are quenched in water at ambient temperature. The temperatures selected for aging treatment are 100, 150, and 2000C and hardness was checked for every 60 minutes of time. The peak hardness obtained because of aging heat treatment is found to be much better than the corresponding sintered compacts. Compacts peak aged at 1000C exhibited better tensile strength than the rest of the other specimens
Accelerating Research
Robert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom
Address
John Eccles HouseRobert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom