English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Carbon was deposited on the surface of an iron powder to study the influence of carbon content and microstructure on defluidization prevention at 823-1 173 K. It was found that at each temperature there existed a minimal carbon content (C-min), below which defluidization occurred and C-min increases with increasing operation temperature. Microstructure of the deposited carbon, tailored by adjusting deposition conditions, showed significant influence on defluidization. Less carbon would be needed to prevent defluidization under a lower rate of carbon deposition since a more uniformly coating of carbon can be obtainable under such conditions. When the fluidizing gas is nitrogen, defluidization will eventually occur after extended time of fluidization even if the initial carbon content is greater than C-min, due to attrition that causes the decrease of carbon content with increasing time of fluidization. However, when the fluidizing gas is 70% CO-30% H-2, defluidization will not occur if the initial carbon content is greater than C-min since the carbon content will increase with increasing time of fluidization due to the further deposition of carbon under the CO-H-2 atmosphere. Furthermore, a fluidizing phase diagram was established for the carbon-coated iron powder and the mechanism of defluidization prevention was explained using a cohesive force based model.

Influence of Content and Microstructure of Deposited Carbon on Fluidization Behavior of Iron Powder at Elevated Temperatures