English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

A summary of Energy Photovoltaics' Phase II work includes the following: (1) EPV has demonstrated that it can sputter a Mo back-contact capable of supporting very high efficiency cell processing. Using EPV Mo, NREL has deposited a 17.1% CIGS cell (no AR coating). EPV believes it can identify the signature of ``good'' Mo. The Mo was produced on EPV's 0.43 m{sup 2} pilot-line equipment; (2) EPV has performed compound synthesis for several classes of materials, namely non-Cu precursor materials, Cu-containing materials, and ternary buffer materials. Using a ternary compound synthesized at EPV (ZIS) as an evaporation source material for the buffer layer, a Cd-free CIGS device has been produced having an efficiency of 11.5% (560 mV, 32.1 mA/cm{sup 2}, FF 64.3%). The ZIS films are photoconductive, and the devices exhibit no dark-light crossover or light soaking effects; (3) EPV initiated the interest of the University of Oregon in capacitance spectroscopy of CIGS devices. An Urbach tail with characteristic energy E0 &lt; 20meV was identified by transient photocapacitance spectroscopy; (4) Small-area CIGS devices were produced in the pilot-line system with an efficiency of 12.0% (581 mV, 30.1 mA/cm{sup 2}, FF 68.7%), and in an R and D-scale system with 13.3% efficiency (569 mV, 34.1 mA/cm{sup 2}, FF 68.1%); (5) An improved linear evaporation source for Cu delivery has been developed and was used for CIGS formation in the pilot-line system. The deposition width is 45 cm. This technological ``tour de force'' allows EPV to build large-area CIGS systems possessing considerable flexibility. In particular, both EPV's FORNAX process and NREL's 3-stage process have been implemented on the pilot line. A CIGS thickness uniformity of 7% over a 40 cm width has been achieved; (6) A 4-head linear source assembly was designed, constructed, and is in use. Flux monitoring is practiced; (7) Large-area CIGS modules were produced with Voc's up to 36.3 V; (8) EPV has started to construct an entirely new CIGS pilot line for scale-up and limited manufacturing purposes. The coating width will be 65 cm; (9) The company's analytical capabilities are currently being upgraded with the installation of ICP and SEM/EDS facilities

Thin-Film CIGS Photovoltaic Technology: Annual Technical Report-Phase II, 16 April 1999-15 April 2000