English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

We found a new nickel sulfide that is isostructural with Fe 3 S. The synthesized nickel sulfide is a non-stoichiometric compound with a Ni deficiency and its composition is Ni 2.90±0.5 S. In situ synchrotron X-ray observations indicate that Ni 3-x S forms above 5.1 GPa and melts incongruently into Ni+liquid up to 10 GPa. The bulk modulus of Ni 3-x S at 300 K was determined to be 140 ± 2 GPa with a fixed K' = 4 by static compression with a liquid pressure medium. The eutectic point of the Ni-NiS system lies between Ni 3 S and Ni 3 S 2  up to 10 GPa and its composition changes from Ni 66.6 S 33.4  at 0.1 MPa to Ni 70.7 S 29.3  at 10 GPa. The eutectic melting temperature of the Ni-NiS system decreases to 5.1 GPa and 720 K as the pressure increases where Ni and α-Ni 3 S 2  are the eutectic solids. On the other hand, the eutectic melting temperature increases with a positive slope above 5.1 GPa where Ni 3 S+α-Ni 3 S 2  is stable under subsolidus conditions. Intermediate compounds appear at a lower pressure in the Ni-NiS system than that for the Fe-FeS system. Ni 3 S 2  is stable at atmospheric pressure and Ni 3 S forms at 5.1 GPa, whereas Fe 3 S 2  and Fe 3 S form at 14 and 20 GPa, respectively. The addition of Ni complicates the melting relationship in the Fe-FeS system at high pressure because of the wider stability field of Ni 3 S. The low-melting temperature of the Fe-Ni-S system plays an important role in the percolative core-formation of planetesimals during planetary accretion.

Stability and bulk modulus of Ni 3 S, a new nickel sulfur compound, and the melting relations of the system Ni-NiS up to 10 GPa