English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

We have examined the long-term durability of a La0.6Sr0.4Co0.2Fe0.8O31¤ (LSCF)­samaria-doped ceria (SDC) composite oxygen electrode with SDC interlayer for reversible solid oxide cells (R-SOCs). A symmetrical cell with the configuration: LSCF­ SDC«SDC interlayer«yttria-stabilized zirconia (YSZ) electrolyte«SDC interlayer«LSCF­SDC, was operated at 900°C and a constant current density of 0.5A cm12 with the top electrode as the anode (O2 evolution). The IR-free overpotentials at both the anode and cathode were virtually constant during 5500 h of operation. The value of ohmic resistance at the anode side (RA) increased slightly, whereas that at the cathode side (RC) increased markedly. The I­E performance of the bottom electrode (operated as the cathode), that was measured from 11.0 to 1.0A cm12 every 1000h, degraded specifically at high current densities. It was found that the thickness, pore size, and porosity in both electrodes were unchanged, but the distribution of the Sr component changed markedly at both the LSCF­SDC/SDC interlayer and SDC interlayer/YSZ interfaces. While the diffusion of the Sr component from the anode was limited within the SDC interlayer, the Sr component from the cathode reached the SDC interlayer/YSZ interface, which could increase the RC, likely due to the formation of SrZrO3. However, the diffusion rates of Sr were found to be noticeably slowed down at dense portions of the SDC interlayer. Hence, it is essential to prepare a dense, uniform SDC interlayer to improve both the durability and performance of R-SOCs.

journal of the ceramic society of japan

High durability of La&lt;sub&gt;0.6&lt;/sub&gt;Sr&lt;sub&gt;0.4&lt;/sub&gt;Co&lt;sub&gt;0.2&lt;/sub&gt;Fe&lt;sub&gt;0.8&lt;/sub&gt;O&lt;sub&gt;3&amp;minus;&amp;delta;&lt;/sub&gt;/samaria-doped ceria (SDC) composite oxygen electrode with SDC interlayer for reversible solid oxide fuel cell/solid oxide electrolysis cell