English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Polycrystalline bulk CaIrO3 as a main phase with minor phases of IrO2 and/or Ca2IrO4 was prepared by spark plasma sintering (SPS) at 1273 K. Metastable CaIrO3 with a perovskite-type structure (pv-CaIrO3) formed by heat-treatment at 1273 K for 43.2 ks and transformed into a post-perovskite structure (ppv-CaIrO3) by heat-treatment at 1273 K for 259.2 ks. The electrical conductivity (σ) of the pv-CaIrO3 specimen decreased from 1.74 × 104 to 1.45 × 104 Sm-1, while the σ of the ppv-CaIrO3 specimen increased from 5.0 × 101 to 9.8 × 102 Sm-1 with increasing temperature from 298 to 1023 K. The Seebeck coefficient (S) of the pv-CaIrO3 specimen was around -44 μVK-1 at room temperature and increase to the highest value of 40 μVK-1 at 1023 K. The S of the ppv-CaIrO3 specimen decreased with increasing temperature and had an almost constant value of about 60 μVK-1 above 600 K. The thermal conductivity (κ) of the ppv-CaIrO3 specimen decreased from 2.7 to 1.2 Wm-1K-1 and that of the pv-CaIrO3 specimen decreased from 1.5 to 1.2 Wm-1K-1 with increasing temperature from 298 to 1023 K. The highest dimensionless figure of merit values (ZT) of the pv-CaIrO3 and the ppv-CaIrO3 specimens were 0.02 and 0.003 at 1023 K, respectively.

Thermoelectricity of CaIrO3 ceramics prepared by spark plasma sintering