English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

Tungstate and tungstate/tartrate inhibitors were used to mitigate the corrosion of fine-grain highstrength (FGHS) reinforcement in simulated concrete pore solutions containing 3.5% NaCl. The physical laws governing the inhibition were investigated using potentiodynamic polarization and electrochemical impedance spectroscopy. The semiconductor characteristics of the corrosion products were analyzed by plotting the Mott–Schottky curves and the corrosion morphology was observed using SEM. A comparison with conventional carbon steel reinforcement (HPB300 steel) was also performed. The results indicated that tungstate is an anodic corrosion inhibitor. Sodium tungstate at concentrations between 0.1 and 0.3 g/L provided good corrosion inhibition, decreasing the corrosion current density from 12.3 μA·cm to 0.326 μA·cm. The carrier density of the corrosion product layer and the electric double-layer capacitance decreased dramatically, while the charge transfer resistance improved significantly. Furthermore, only a few pits formed on the FGHS reinforcement. The tungstate/tartrate mixed inhibitor was found to display the advantages of a single inhibitor, although no synergistic effect was observed. When the inhibitor was absent, the corrosion resistance properties of FGHS reinforcement were clearly inferior to those of HPB300 steel. However, the addition of tungstate or tungstate/tartrate mixed inhibitor led to improved indicators of corrosion resistance for the FGHS sample relative to HPB300 steel.

Corrosion Inhibition Effect of Tungstate on Fine-Grain High- Strength Reinforcement in Simulated Concrete Pore Solutions Containing Chloride Ions