English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

The purpose of this study was to investigate the effect of annealing to the hardness of high Y2O3-oxide dispersion strengthened (ODS) ferritic steels. The samples were prepared by mechanical alloying method followed by Cold Isostatic Pressing (CIP). After compaction process, the samples were sintered at 1100°C for 1 h in a tube furnace. The crystal structure and morphology of samples were analyzed by X-ray Diffraction (XRD) measurement and characterized by using field emission scanning electron microscope (FESEM), respectively. The hardness of samples was measured by using a micro-Vickers hardness tester with a load of 200 gf at annealing temperature of 600°C, 800°C and 1000°C, respectively. The Vickers hardness value (HV0,2) versus annealing temperature graph showed that the hardness of all samples started to decrease at temperature of 600°C due to grain growth. The hardness value of all samples (1Y and 5Y) identified at this annealing temperature is 855 HV0,2 and 808 HV0, 2, respectively.

The Effect of Annealing to the Hardness of High Y2O3-Oxide Dispersion Strengthened (ODS) Ferritic Steels