English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

En este estudio se fabricaron diferentes materiales (base cobre) bajo las mismas condiciones de molienda: molino empleado fue un SPEX 8000D, atmósfera de argón, acido esteárico, RBP=10:1, con tiempos varia-bles desde 1 hasta 120 horas, con el objetivo de comparar los cambios microestructurales durante el proceso de: Cobre puro, Aleaciones Cu-Ni, Aleaciones Cu-Zr y aleaciones Cu-Ni-Zr. Las muestras, tras la molienda, fueron analizadas mediante difracción de rayos X, microscopía electrónica de transmisión y calorimetría dife-rencial de barrido. De acuerdo a los resultados, el cobre al ser sometido al proceso alcanza un tamaño de cris-talita que se hace asintótico a partir de las 5 horas, mientras que en el sistema Cu-Ni, en vez de apreciarse un refinamiento microestructural a ese mismo periodo, se advierte una total solubilización del níquel en cobre (40-60 y 50-50) y de cobre en níquel (60-40). Por su parte, en el sistema binario Cu-Zr, se encontró, tam-bién para 5 horas, que el sistema estaba prácticamente amorfizado (60-40 y 50-50) al igual que en el caso de las aleaciones ternarias Cu-Ni-Zr (60-10-30 y 50-10-40).In this study, different, copper-based materials were fabricated under equal milling conditions (SPEX 8000D, argon atmosphere, stearic acid, BPR=10:1) and variable amounts of time, from 1 to 120 hours, in order to compare the microstructural changes during the process. The materials were: Pure copper; Cu-Ni alloys; CuZr alloys; and Cu-Ni-Zr alloys. Subsequent to milling, the samples were measured with X-Ray Diffraction, Electron Transmission Microscopy, and Differential Scanning Calorimetry. According to the results, copper, upon being subjected to the process, reaches a crystallite size that tends towards an asymptote starting at 5 hours. In the Cu-Ni system, instead of observing a microstructural refinement during this same period, there was rather a total solubilization of the nickel into the copper (40-60 and50-50), and of the copper into the nickel (60-40). As for the Cu-Zr binary system, it was found that, for five hours as well, the system was practically amorphous (60-40 and 50-50), a condition also present in the Cu-Ni-Zr ternary alloys (60-10-30 and 50-10-40).Fil: Rojas, Paula. Pontificia Universidad Catolica de Valparaiso; Chile. Universidad Adolfo Ibañez; ChileFil: Martínez, Carola. Pontificia Universidad Catolica de Valparaiso; Chile. Pontificia Universidad Catolica de Valparaiso; ChileFil: Viancos, Francisco. Pontificia Universidad Catolica de Valparaiso; ChileFil: Aguilar, Claudio. Universidad Técnica Federico Santa María. Departamento de Ingeniería Metalúrgica y Materiales; ChileFil: Guzmán, Danny . Universidad de Atacama. Departamento de Ingeniería Metalúrgica y Materiales; ChileFil: Zelaya, Maria Eugenia. Comision Nacional de Energia Atomica. Gerencia del Area de Investigaciones y Aplicaciones no Nucleares. Gerencia de Fisica (CAB); Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentin

Fabricación de vidrios metálicos base cobre: evolución de las fases durante el procesode aleación mecánica