English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

Misturas de PS/EVA, preparadas sob diferentes condições numa câmara de mistura interna, foram avaliadas quanto ao grau de continuidade ou co-continuidade de fases. Três técnicas foram empregadas: ensaio de extração seletiva, microscopia eletrônica de varredura (SEM) e análise térmica dinâmico-mecânica (DMTA). As diferentes temperaturas empregadas no processamento das misturas afetam substancialmente a faixa de co-continuidade e o ponto de percolação. Pôde-se observar que temperaturas mais altas de processamento acarretam num estreitamento da faixa de co-continuidade. As misturas PS/EVA na composição 60/40 %vol apresentaram uma morfologia do tipo co-contínua, independente da temperatura empregada no processamento ou do tipo de EVA. Na composição complementar, PS/EVA (40/60 % vol), a morfologia passa a ser dependente tanto da temperatura de processamento como do tipo de EVA empregado. As morfologias obtidas por SEM confirmaram os resultados obtidos nos ensaios de extração seletiva. A técnica de DMTA mostrou ser uma boa alternativa para correlacionar estrutura molecular e morfologia. Polystyrene/ethylene <FONT FACE=Symbol>¾</FONT> vinyl acetate (EVA) copolymer blends were prepared in an internal mixer with the purpose of investigating the cocontinuous range. The effect of the processing temperature and the chemical composition of the EVA component was studied by scanning electron microscopy (SEM), selective extraction experiments and dynamic mechanical analyses (DMTA). A decrease of mixing temperature and an increase of vinyl acetate content in the EVA component resulted in a shift of the percolation threshold of dispersed PS to lower concentrations. The range where cocontinuous structure can be found depends upon the processing temperature and the EVA nature. The results obtained from selective extraction experiments are in agreement with those obtained from SEM. The changes in phase morphology with the composition and temperature processing was also confirmed by DMTA results

Morfologia Co-Contínua na Mistura Poliestireno/Copolímero de Etileno-Acetato de Vinila