English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

In order to investigate the effect of natural convection in columnar to equiaxed transition (CET), Al-3.0wt.%Cu and Al-3.0wt.%Cu-5.5wt.%Si alloys ingots were obtained during the transient horizontal directional solidification (THDS). Aiming to analyze the effect of superheat in the formation of the macrostructure in ternary Al-Cu-Si alloy, the experiments were conducted with three superheat temperatures above the liquidus temperature of the ternary alloy. A water-cooled solidification experimental device was used. Continuous temperature measurements were made during solidification at different positions in the casting and the data were automatically acquired. Thermal analysis has been applied to determine the thermal parameters such as growth rate (VL), cooling rate (TR) and temperature gradient (GL), whose values have been interrelated with the CET. The observation of the macrostructures has indicated that the resulting thermosolutal convection combined with superheat seem to favor the transition, which did not occur in a single plane, for all ingots obtained, i.e., it has been seen in a range of positions in ingots. The addition of Si element in binary Al-Cu alloy anticipates the CET. A comparison with experimental results for CET occurrence in different growth directions has been carried out.

On the Natural Convection in the Columnar to Equiaxed Transition in Directionally Solidified Aluminum-based Binary and Multicomponent Alloys