English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

Hishinuma et al. has established a new Powder-In-Tube (PIT) process using a high Ga content Cu-Ga compound in order to improve the superconducting property of the V3Ga compound wire. In this study, we investigated the microstructure of this high Ga content Cu-Ga/V composite superconducting wire. Three different contrasts of the matrix, V-Ga phase and Cu-Ga core were observed by SEM observation in the cross section of 19-multifilament wire. The V-Ga phase was confirmed by SEM mapping. The area fraction of V-Ga phase increased when Ga content increased from 30% to 50%. Thin film sample with V-Ga phase for TEM observation was fabricated by FIB. Selected area diffraction pattern was obtained for V matrix, V-Ga phase and Cu-Ga core. The ratio of V to Ga in V-Ga phase was close to V3Ga according to the EDS result. The interface between V matrix and V-Ga phase was linear, while the interface between Cu-Ga core and V-Ga phase was not linear. On the other hand, there were some granular grains observed in V-Ga phase around Cu-Ga core.

Microstructure of V<sub>3</sub>Ga Superconducting Wire Using Cu/V with High Ga Contents