English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Poly(lactic acid) (PLA)-hemp-nanosilica (PHS) composites were prepared by impregnation of hemp woven fabric with PLA solution. Nanosilica was dispersed in the PLA solution to introduce a matrix reinforcing nanophase within the composite. The melting behavior of PLA composites was obtained by using differential scanning calorimetry (DSC) and modulated-temperature DSC (mT-DSC). Multiple melting which appeared in the non-isothermal heating curve showed that the temperature of a low melting peak increased when using a slower scanning rate. The incorporation of nanosilica in PLA composites affected the melting temperature ( T   m  ) and sufficiently formed nucleation sites that promoted the growth of PLA crystals. Composites analyzed by a temperature-modulated program showed a broad exothermic peak before the melting peak in the non-reversing heat capacity and endothermic melting in the reversing heat capacity curve. This behavior was explained by a process of partial melting, recrystallization and remelting (mrr). The mT-DSC resolved that hemp fiber induced recrystallization and nanosilica acted as an effective nucleating agent, which promoted small and imperfect crystals that changed successively into more stable crystals through a melt-recrystallization process.

Multiple melting behavior of poly(lactic acid)-hemp-silica composites using modulated-temperature differential scanning calorimetry