English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

The main objective of this investigation is to analyze the influence of DCT cycles on microstructural evolution, surface roughness, hardness and dimensional stability of AISI D2 tool steel for cutting tools and dies applications. The cryogenic quenching was done using gaseous nitrogen. The AISI D2 tool steel was subjected to two DCT cycle: DCT-I (Hardening + DCT + tempering) and DCT-II (Hardening + tempering + DCT). The dimensional stability of AISI D2 tool steel was evaluated using standard Navy C-ring test. The coordinate measuring machine (CMM) was employed for the precise measurement of Navy C-ring subjected to different DCT cycle. The surface roughness was evaluated with  Ra    (arithmetic mean roughness) and  Rt    (total height of roughness profile) values using surface roughness tester. The microstructural features were analyzed using optical (OM) and scanning electron microscopy (SEM). The electrical resistivity and hardness of treated samples were measured using micro-Ohm meter and Vickers microhardness tester. Results showed that AISI D2 tool steel treated with DCT-I cycle exhibited greater surface finish, hardness and dimensional stability compared to DCT-II cycle. It is mainly attributed to the greater precipitation of finer carbides and balancing of tensile-compressive residual stresses.

materials testing

Effect of deep cryogenic processing cycles on surface roughness, dimensional stability and microstructure of high carbon high chromium tool steel for cutting tool and dies applications