English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Aluminum coating on 1Cr18Ni9Ti stainless steel was prepared by magnetron sputtering method. The specimens were treated with pre-oxidation (PO) or vacuum diffusion annealing (VA). Hot corrosion resistance of the coatings beneath the deposits of Na 2 SO 4  at 1050 °C was investigated. Corrosion products were analyzed by XRD and SEM. Results show that the presence of coating could improve the corrosion resistance of stainless steel. FeAl phase appeared after VA at 600 °C, which enhanced cohesive force between the coating and the substrate, and reduced the oxidation and sulfidation rate. PO treatment can protect the substrate more effectively than VA treatment for metastable Al 2 O 3  formed during PO treatment can be translated to stable Al 2 O 3  more quickly at high temperatures. The corrosion products of the two kinds of specimens with aluminum coating were both composed of Al 2 O 3 , a little amount of FeS and Fe 2 O 3  after 24 h corrosion. Al 2 O 3  was formed mainly in the coatings, FeS was mainly distributed in the interface between coating and substrate of the specimens, and a small amount of FeS was distributed in the substrate. Al 2 O 3  film remained intact after 24 h corrosion, and kept its protective effect on the substrate.

Effect of Different Treatment on Corrosion Resistance of Sputtered Al Coating on Stainless Steel