English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

The creep and wear behaviour of pressed UHMWPE and extruded UHMWPE was compared, taking Chirulen and extruded UHMWPE of the Lennite type as examples. Using the ring-on-disc test, the wear and deformation volumes per 360,000 cycles were determined. The static tests were performed at surface pressures of 5.62 MPa and 9.37 MPa, while the test duration was 41.86 and 100 hours, respectively. The surface pressures result from the axial forces of 900 N and 1500 N, respectively, and a ring surface analogous to the DIN 58,835 and ISO 6474 standards. Between conventionally pressed and the extruded UHMWPE material differences of up to 350% in the sums of wear and deformation were found. It was noted that already at low surface pressures the extruded UHMWPE is more susceptible to creep deformation than is the conventionally pressed material, and that this effect dramatically increases at high surface pressures.

biomedizinische technik

Der Einfluß des Verarbeitungsverfahrens auf die Kriech- und Abriebeigenschaften von UHMWPE - The Influence of the Manufacturing Process on Creep and Wear Properties of UHMWPE