English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

This paper reports on theoretical calculations and fabrication by molecular beam epitaxy of wide-gap ITVI heterostructures emitting in the 'true" yellow range (560-600 nm) at room temperature. The active region of the structures comprises CdSe quantum dot active layer embedded into a strained Zn1-xCdxSe (x = 0.2-0.5) quantum well surrounded by a Zn(S,Se)/ZnSe superlattice. Calculations of the CdSe/(Zn,Cd)Se/Zn(S,Se) quantum dot quantum well luminescence wavelength performed using the envelope-function approximation predict rather narrow range of the total Zn1-xCdxSe quantum well thicknesses (d approximate to 2-4 nm) reducing efficiently the emission wavelength, while the variation of x (0.2-0.5) has much stronger effect. The calculations are in a reasonable agreement with the experimental data obtained on a series of test heterostructures. The maximum experimentally achieved emission wavelength at 300 K is as high as 600 nm, while the intense room temperature photoluminescence has been observed up to lambda = 590 nm only. To keep the structure pseudomorphic to GaAs as a whole the tensile-strained surrounding ZnS0.17Se0.83/ZnSe superlattice were introduced to compensate the compressive stress induced by the Zn1-xCdxSe quantum well. The graded-index waveguide laser heterostructure with a CdSe/Zn0.65Cd0.35Se/Zn(S,Se) quantum dot-quantum well active region emitting at lambda = 576 nm (T = 300 K) with the 77 to 300 K intensity ratio of 2.5 has been demonstrated.

CdSe/ZnCdSe Quantum Dot Heterostructures for Yellow Spectral Range Grown on GaAs Substrates by Molecular Beam Epitaxy