English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Background  The repair of large bone defects is a great challenge in clinical practice. In this study, copper-loaded-ZIF-8 nanoparticles and poly (lactide- co -glycolide) (PLGA) were combined to fabricate porous PLGA/Cu(I)@ZIF-8 scaffolds using three-dimensional printing technology for infected bone repair.    Methods  The surface morphology of PLGA/Cu(I)@ZIF-8 scaffolds was investigated by transmission electron microscopy and scanning electron microscopy. The PLGA/Cu(I)@ZIF-8 scaffolds were co-cultured with bacteria to determine their antibacterial properties, and with murine mesenchymal stem cells (MSCs) to explore their biocompatibility and osteoconductive properties. The bioactivity of the PLGA/Cu(I)@ZIF-8 scaffolds was evaluated by incubating in simulated body fluid.    Results  The results revealed that the PLGA/Cu(I)@ZIF-8 scaffolds had porosities of 80.04 ± 5.6% and exhibited good mechanical properties. When incubated with H 2 O 2 , Cu(I)@ZIF-8 nanoparticles resulted generated reactive oxygen species, which contributed to their antibacterial properties. The mMSCs cultured on the surface of PLGA/Cu(I)@ZIF-8 scaffolds were well-spread and adherent with a high proliferation rate, and staining with alkaline phosphatase and alizarin red was increased compared with the pure PLGA scaffolds. The mineralization assay showed an apatite-rich layer was formed on the surface of PLGA/Cu(I)@ZIF-8 scaffolds, while there was hardly any apatite on the surface of the PLGA scaffolds. Additionally, in vitro,  Staphylococcus aureus  cultured on the PLGA/Cu(I)@ZIF-8 scaffolds were almost all dead, while in vivo inflammatory cell infiltration and bacteria numbers were dramatically reduced in infected rats implanted with PLGA/Cu@ZIF-8 scaffolds.    Conclusion  All these findings demonstrate that PLGA/Cu(I)@ZIF-8 scaffolds possess excellent antibacterial and osteoconductive properties, as well as good biocompatibility and high bioactivity. This study suggests that the PLGA/Cu(I)@ZIF-8 scaffolds could be used as a promising biomaterial for bone tissue engineering, especially for infected bone repair.

Preparation of antibacterial and osteoconductive 3D-printed PLGA/Cu(I)@ZIF-8 nanocomposite scaffolds for infected bone repair