English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

This work verified the effect caused by adding the surfactant in the high speed/energy milling in order to obtain Pr12Fe65.9Co16B6Nb0.1 magnetic nanopowders. The first part of this work involved the magnetic powder obtainment through the process of hydrogenation, disproportionation, desorption and recombination (HDDR). The pressure of H2 during the hydrogenation and disproportion steps was 930 mbar and the temperature of desorption and recombination was 840 oC. Initially, the HDDR powders were subjected a highspeed milling process at 900 rpm, with quantity variations of the milling medium (cyclohexane) and without the addition of oleic acid. Then, the HDDR powders were subjected to the milling process with the addition of oleic acid and with milling time variations. After the milling process, heat treatments of the powder were carried out at 700 °C or 800 °C for 30 minutes in order to obtain the crystallization of the powder. By performing the procedures, it was verified that the milling efficiency improved with the addition of 6.6 ml of cyclohexane as the milling medium and with the addition of oleic acid. It was determined that for the surfactant additions of 0.02 ml to 0.05 ml, with a milling time of up to 360 minutes, powder agglomeration does not occur in the milling pot and the milling efficiency is higher than 90%. The second stage of this work involved the magnetic powders characterization obtained by using vibrating sample magnetometer, scanning electron microscopy, transmission electron microscopy and X-ray diffraction. Through the characterizations it was found that the powder’s magnetic properties improved when the addition of oleic acid in a high-speed /energy milling occurred. It was also verified that the α-Fe phase, present in the powder, shows a crystallite size decrease (from 35 nm to ~ 10 nm) when the time milling variation occurred; meanwhile, the crystallinity degree was lower in the Pr2Fe14B phase when the time milling variations was carried out.

Efeitos da adição de surfactante e moagem de alta velocidade em pós magnéticos à base de Pr-Fe-B obtidos via HDDR