English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

In this paper, 156 mm×156 mm boron-doped Czochralski silicon (Cz-Si) wafers were fabricated into PERC solar cells by using the industrial standard process; then, the as-prepared PERC solar cells were treated by the regeneration process using electrical injection and heating and the effects of different regeneration processes (temperature, time, and injection current) on the anti-light-induced degradation (anti-LID) performance of the PERC solar cells were investigated. The results show that under the condition of 10 A injection current and 30 min processing time, the optimal processing temperature is about 180°C for PERC solar cells to obtain the best anti-LID performance. Under the conditions of a temperature of 180°C, an injection current of 10 A, and a processing time of 0-30 min, the anti-LID performance of the PERC solar cells is enhanced with the increase in the processing time. When the processing time is 20 and 30 min, the efficiency, the short-circuit current, and the open-circuit voltage of the processed PERC solar cells are slightly higher than the initial values before the regeneration and remain stable in the subsequent 12-hour light degradation process at 45°C and 1-sun illumination. At a temperature of 180°C and a processing time of 30 min, the injection current of 6 A is enough to obtain a good regeneration effect, but the optimal injection current is around 10 A.

Study on the Electrical Injection Regeneration of Industrialized B-Doped Czochralski Silicon PERC Solar Cells