English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

The compositions and formation process of f-CaO in BOF slag were revealed and simulated to understand its expansion rules and why its hydration activity is low. BSE showed the compositions of f-CaO, which included calcium iron phase and calcium iron manganese phase, were diverse. The hydration activity sequence was Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; only Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 were hard to hydrate, and the volume expansion rates of the tricomponent f-CaO varied with different compositions. Inductively, in BOF slag, the hydration activity sequence was solid solutions CaO-FeOx and CaO-FeOx-MnOy in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; the volume expansion rates of tricomponent f-CaO changed with different compositions, and CaO-FeOx and CaO-FeOx-MnOy were difficult to hydrate. The reason why solid solutions CaO-FeOx and CaO-FeOx-MnOy were hard to hydrate was that their hydration reaction driving force, which is the absolute value of standard molar reaction Gibbs functions, decreased.

Simulated Experiment Study of Factors Influencing the Hydration Activity of f-CaO in Basic Oxygen Furnace Slag