English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

Low-density polyethylene was thermo-oxidatively degraded at 170 °C, i.e., degraded in the presence of air, by a one thermal cycle (1C) treatment during times between 30 and 90 min, and by a two thermal cycles (2C) treatment, i.e., after storage at room temperature, an already previously degraded sample was further degraded during times between 15 and 45 min. Characterization methods include gel permeation chromatography (GPC), Fourier transform infrared (FTIR) spectroscopy, as well as linear and nonlinear rheology. A reduction of molar mass was detected for all degraded samples by GPC, as well as an increase of the high molar mass fraction of the 1C sample degraded for the longest time. Intrinsic viscosity measurements indicate also a reduction of molar mass with increasing degradation times for both 1C and 2C samples. Thermo-oxidation is confirmed for 1C and 2C samples by analyzing specific indices in FTIR. Linear viscoelasticity seems to be in general only marginally affected by thermo-oxidative exposur...

Increase of long-chain branching by thermo-oxidative treatment of LDPE: Chromatographic, spectroscopic, and rheological evidence