English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

We report the results of a new experimental setup to measure the mechanical loss of coating layers on a thin sapphire disk at cryogenic temperatures. Some of the authors previously reported that there was no temperature dependence of the mechanical loss from a multilayer tantala/silica coating on a sapphire disk, both before and after heat treatment, although some reports indicate that Ta2O5 and SiO2 layers annealed at 600 °C have loss peaks near 20 K. Since KAGRA—the Japanese gravitational-wave detector, currently under construction—will be operated at 20 K and have coated sapphire mirrors, it is very important to clarify the mechanical loss behavior of tantala/silica coatings around this temperature. We carefully investigate a tantala/silica-coated sapphire disk with the new setup, anneal the disk, and then investigate the annealed disk. We find that there is no distinct loss peak both before and after annealing under particular conditions. The mechanical loss for the unannealed disk at 20 K is about 5×10−4, as previously reported, while that for the annealed disk is approximately 6.4×10−4.

Mechanical loss of a multilayer tantala/silica coating on a sapphire disk at cryogenic temperatures: Toward the KAGRA gravitational wave detector