English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

Powder metallurgy (PM) steel with enhanced density is essential for meeting the demands on high strength and high-performance applications. In this study, cold isostatic pressing (CIP) is applied for consolidating water-atomised iron and Cr-alloyed steel powder to reach about 95% densification before sintering. Additionally, the effect of the lubricant and graphite addition on the compressibility of the different base powder types was evaluated. The maximum green densities of ≈7.55 g cm −3  for iron powder and ≈7.45 g cm −3  for Cr-alloyed powder were reached after CIP at 800 MPa. The sintering at 1250°C with added graphite allowed to achieve increased densification to ≈7.60 g cm −3  for the iron and ≈7.50 g cm −3  for Cr-alloyed grades, respectively. These levels were sufficient for surface pore closure, which allowed the application of the capsule-free hot isostatic pressing (HIP) after sintering to reach full density. This approach paves the way for manufacturing large-sized PM components.

powder metallurgy

Capsule-free hot isostatic pressing of sintered steel to full density using water atomised iron and Cr-alloyed powder consolidated by cold isostatic pressing