English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

This paper describes a method to optimally combine wide band gap Al2O3 with high dielectric constant (high-κ) Ta2O5 for gate dielectric applications. (Ta2O5)x(Al2O3)1−x thin films deposited by thermal atomic layer deposition (ALD) on GaN-capped AlxGa1−xN/GaN high electron mobility transistor (HEMT) structures have been studied as a function of the Ta2O5 molar fraction. X-ray photoelectron spectroscopy shows that the bandgap of the oxide films linearly decreases from 6.5 eV for pure Al2O3 to 4.6 eV for pure Ta2O5. The dielectric constant calculated from capacitance-voltage measurements also increases linearly from 7.8 for Al2O3 up to 25.6 for Ta2O5. The effect of post-deposition annealing in N2 at 600 °C on the interfacial properties of undoped Al2O3 and Ta-doped (Ta2O5)0.12(Al2O3)0.88 films grown on GaN-HEMTs has been investigated. These conditions are analogous to the conditions used for source/drain contact formation in gate-first HEMT technology. A reduction of the Ga-O to Ga-N bond ratios at the oxide...

journal of applied physics

Comparative analysis of the effects of tantalum doping and annealing on atomic layer deposited (Ta2O5)<i>x</i>(Al2O3)1−<i>x</i> as potential gate dielectrics for GaN/AlxGa1−xN/GaN high electron mobility transistors

Comparative analysis of the effects of tantalum doping and annealing on atomic layer deposited (Ta2O5)x(Al2O3)1−x as potential gate dielectrics for GaN/AlxGa1−xN/GaN high electron mobility transistors