English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

N-type Bi₂Te₂.₇Se₀.₃ bulk thermoelectric materials with peak ZT values up to ∼1 were examined by transmission electron microscopy and electron diffraction. Two nanostructural features were found: (i) a structural modulation of ∼10 nm, which consisted of nanorods with crystalline and nearly amorphous regions, having the rod axes normal to (0,1,5)-type planes, and wave vector normal to (1,0,10)-type planes and (ii) non-stoichiometric ordered Bi-rich nanoparticles. The presence of the structural modulation was not influenced by the ion milling energy or temperature in this study while the non-stoichiometric ordered nanoparticles were only observed when ion milling at low temperatures and low energy was used. It is proposed that both the structural modulation of ∼10 nm and the presence of non-stoichiometric nanoparticles are responsible for the low lattice thermal conductivity (∼0.6 W/mK) of the Bi₂Te₂.₇Se₀.₃ bulk thermoelectric materials studied.United States. Dept. of Energy. Office of Science (Solar-Thermal Energy Conversion Center, Award No. DE-FG02-09ER46577

Disordered stoichiometric nanorods and ordered off-stoichiometric nanoparticles in n-type thermoelectric Bi2Te2.7Se0.3