English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

CuInSe2 was studied in the as-grown state and after low-temperature (4 K) 2 MeV electron irradiation. The positron bulk lifetime of 235 ps was measured for the unirradiated sample. The positron bulk lifetime was theoretically calculated and is in good agreement with the experimental value. In addition, the defect-related lifetimes for mono-, di-, and trivacancies are theoretically determined. An increased average positron lifetime indicated after electron irradiation the appearance of open-volume defects, most probably of divacancy type. The disappearance of this defect was observed during annealing below 250 K. Other defects were formed leading to a divacancy signal at least stable up to 600 K in the temperature range above 450 K.Peer reviewe

Study of defects in electron irradiated CuInSe2 by positron lifetime spectroscopy