English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Chemical solution deposition as a simple method for preparation of oxide films is used to fabricate misfit structured Ca3Co4O9 thermoelectric films using cheap precursors, Ca and Co acetates, which opens up a simple route to fabricate large-area Co-based oxide thermoelectric films. The results show that when the annealing temperature is higher than 800°C crystallized Ca3Co4O9 films can be obtained on single-crystal LaAlO3 substrates, whereas the Ca3Co4O9 films are amorphous for lower annealing temperatures. Experimental evidence shows that the amorphous Ca3Co4O9 films behave like semiconductors with enhanced resistivity and Seebeck coefficient within the measured temperature range. The magnetoresistance is positive indicating the absence of long-range order of the Co-ion spins. For the crystallized Ca3Co4O9 films, it can be seen that the thinner films show the characteristics of spontaneous dewetting induced by the stress, which suggests that it is possible to prepare nanostructured Ca3Co4O9 films through...

Growth of Ca3Co4O9 films: Simple chemical solution deposition and stress induced spontaneous dewetting