English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

The strain relaxation of pseudomorphic Si1-xGex layers (x=0.21,...,0.33) was investigated after low-dose Si+ ion implantation and annealing. The layers were grown by molecular-beam epitaxy or chemical vapor deposition on Si(100) or silicon-on-insulator. Strain relaxation of up to 75% of the initial strain was observed at temperatures as low as 850 degreesC after implantation of Si ions with doses below 2x10(14) cm(-2). We suggest that the Si implantation generates primarily dislocation loops in the SiGe layer and in the underlying Si which convert to strain relaxing misfit segments. The obtained results are comparable to strain relaxation achieved after He+ implantation with doses of 1-2x10(16) cm(-2). (C) 2004 American Institute of Physics

Strain relaxation of pseudomorphic Si1−xGex∕Si(100) heterostructures after Si+ ion implantation