English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Open

Presents the pdf analysis as premium feature

PDF Analysis

Insights

Presents the summarisation as premium feature

Summarisation

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Long-lasting phosphorescence was observed at 510 nm in a Sn 2+-Cu2+ codoped Na2O-CaO-SiO2 glass at room temperature under UV illumination of 254 nm. When the glass was compressed under 3, 6, and 9 GPa, the phosphorescence shifted to 465 nm and its decay rate became shorter. The optical absorption spectra of the samples changed after compression, showing that the cupric ions were reduced to the cuprous ions. The high-pressure treatment also resulted in a lower-energy shift in the absorption edge. It was suggested that Sn2+ ions act as hole trapping centers, while oxygen vacancies surrounding by Ca2+ ions as well as active sites in the glass matrix, i.e., as electron trapping centers. © 2002 American Institute of Physics.

Long-lasting phosphorescence in Sn2+–Cu2+ codoped silicate glass and its high-pressure treatment effect