English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

The dislocation structure in sheet specimens of 99.999 wt % aluminium single crystals was observed by transmission electron microscope (TEM) in order to explore the micromechanism corresponding to the appearance and disappearance of the internal-friction peak around 365°C (f = 1 HZ). /1/ Internal-friction measurements were made with an inverted torsion pendulum on sheet specimens having a thickness of 1 mm or smaller and a width of 4.5 mm. The same specimen was thinned down after the internal-friction measurements by chemical polishing and a double jet electrolytic polishing to films about 700 nm thick for TEM observations. The results of internal-friction measurements were compared with TEM observations

le journal de physique colloques

ELECTRON MICROSCOPIC OBSERVATION ON THE DISLOCATION CONFIGURATION CORRELATIVE WITH THE HIGH-TEMPERATURE INTERNAL-FRICTION PEAK IN 99.999 wt % SINGLE-CRYSTAL ALUMINIUM