English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Research was carried out on the incorporation of divalent cobalt cations into the crystalline structure of MgF 2 to form Mg  x  Co 1- x  F 2 binary fluorides, which had not been investigated before. The above fluorides were obtained by the precipitation from aqueous solution of magnesium and cobalt nitrates with ammonium fluoride. Binary fluorides containing 0.6, 7.5 and 37.7 mol% CoF 2 were prepared. The effects of treatment temperature (300, 400 °C) and atmosphere (oxidizing or reducing) on the structure (XRD, TPR-H 2 , UV-Vis), texture (low-temperature N 2 adsorption), surface composition (XPS) and surface acidity (NH 3 -TPD) of the binary fluorides were determined. It has been found that in Mg  x  Co 1- x  F 2 an isomorphic substitution occurs of Mg 2+ cations by Co 2+ cations which results in the formation of a rutile-type solid solution. The obtained binary fluorides are characterized by a mesoporous structure and relatively large surface area. It has been found that thermal treatment of the binary fluorides in oxidizing conditions results in the oxidation of CoF 2 to Co 3 O 4 even at 300 °C; therefore it is not possible to obtain pure Mg  x  Co 1- x  F 2 binary fluorides in the presence of air. The preparation of the latter requires reducing conditions, namely thermal treatment of dry precipitate at 300 °C in an atmosphere of hydrogen. If the treatment is conducted at a higher temperature (400 °C), CoF 2 undergoes a partial reduction to metallic cobalt. An XPS study has shown the presence of hydroxyl groups in the investigated samples. However, these are solely surface groups because their presence was not detected by XRD measurements. The binary fluorides obtained by our method are characterized by a very narrow optical energy gap (5.31-3.50 eV), considerably narrower than that recorded for bulk fluorides. Measurements of temperature-programmed desorption of ammonia have shown that the incorporation of cobalt cations into the crystal structure of MgF 2 results in a decrease in the surface acidity of the binary fluorides.

rsc advances

Synthesis and characterization of MgF<sub>2</sub>–CoF<sub>2</sub> binary fluorides. Influence of the treatment atmosphere and temperature on the structure and surface properties

Synthesis and characterization of MgF2–CoF2 binary fluorides. Influence of the treatment atmosphere and temperature on the structure and surface properties

Synthesis and characterization of MgF₂–CoF₂ binary fluorides. Influence of the treatment atmosphere and temperature on the structure and surface properties