English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

A three layer membrane (TLM) of polybenzimidazole/graphite oxide/polybenzimidazole (PBI/GO/PBI) has been fabricated as an electrolyte for intermediate temperature polymer exchange membrane fuel cells (IT-PEMFCs). The membrane is prepared by encapsulating a GO layer with two single PBI membranes via a layer-by-layer procedure and subsequently imbibed with phosphoric acid (PA). The TLM exhibits a lower swelling ratio than that of the pristine PBI membrane at the same PA loading time. The mechanical strength of the TLM could reach 28.6 MPa at 150 °C, significantly higher than that of a PBI membrane (12.2 MPa). The TLM is loaded with a PA amount of 2.23H3PO4 molecules per repeat unit (PRU), which provides a proton conductivity of 0.0138 S cm−1 at 150 °C. The three layer structure promotes a membrane for PEMFCs with lower PA leakage and material corrosion. The fuel cell performance based on TLM exhibits a peak power density of 210 mW cm−2 at 150 °C.

A polybenzimidazole/graphite oxide based three layer membrane for intermediate temperature polymer electrolyte membrane fuel cells