English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

We report on a new route to grow epitaxial copper (Cu) ultra-thin films (up to 150 nm thick) at ambient temperature on Si(001) wafers covered with native oxide without any prior chemical etching or plasma cleaning of the substrate. It consists of a single-step deposition process using high power impulse magnetron sputtering (HiPIMS) and substrate biasing. For a direct current (DC) substrate bias voltage of −130 V, Cu/Si heteroepitaxial growth is achieved by HiPIMS following the Cu(001) [100]//Si(001) [110] orientation, while under the same average deposition conditions, but using conventional DC magnetron sputtering, polycrystalline Cu films with [111] preferred orientation are deposited. In addition, the intrinsic stress has been measured  in situ  during growth by real-time monitoring of the wafer curvature. For this particular HiPIMS case, the stress is slightly compressive (−0.1 GPa), but almost fully relaxes after growth is terminated. As a result of epitaxy, the Cu surface morphology exhibits a regular pattern consisting of square-shaped mounds with a lateral size of typically 150 nm. For all samples, X-ray diffraction pole figures and scanning/transmission electron microscopy reveal the formation of extensive twinning of the Cu {111} planes.

Epitaxial growth of Cu(001) thin films onto Si(001) using a single-step HiPIMS process