English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Single crystals of a new iron-containing oxide, Ba(4)KFe(3)O(9), were grown from a hydroxide melt, and the crystal structure was determined by single-crystal X-ray diffraction. This ferrite represents the first complex oxide containing isolated 6-membered rings of corner-sharing FeO(4) tetrahedra. Mössbauer measurements are indicative of two tetrahedral high-spin Fe(3+) coordination environments. The observed magnetic moment (~3.9 μ(B)) at 400 K is significantly lower than the calculated spin-only (~5.2 μ(B)) value, indicating the presence of strong antiferromagnetic interactions in the oxide. Our density functional theory calculations confirm the strong antiferromagnetic coupling between adjacent Fe(3+) sites within each 6-membered ring and estimate the nearest-neighbor spin-exchange integral as ~200 K; next-nearest-neighbor interactions are shown to be negligible. The lower than expected effective magnetic moment for Ba(4)KFe(3)O(9) calculated from χT data is explained as resulting from the occupation of lower-lying magnetic states in which more spins are paired. X-band (9.5 GHz) electron paramagnetic resonance (EPR) spectra of a powder sample consist of a single line at g ~ 2.01 that is characteristic of Fe(3+) ions in a tetrahedral environment, thus confirming the Mössbauer results. Further analysis of the EPR line shape reveals the presence of two types of Fe(6) magnetic species with an intensity ratio of ~1:9. Both species have Lorentzian line shapes and indistinguishable g factors but differ in their peak-to-peak line widths (δB(pp)). The line-width ratio δB(pp)(major)/δB(pp)(minor) ~ 3.6 correlates well with the ratio of the Weiss constants, θ(minor)/θ(major) ~ 4.

Ba4KFe3O9: A Novel Ferrite Containing Discrete 6-Membered Rings of Corner-Sharing FeO4 Tetrahedra

Ba₄KFe₃O₉: A Novel Ferrite Containing Discrete 6-Membered Rings of Corner-Sharing FeO₄ Tetrahedra