English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Au nanoparticles with a mean diameter of 20 nm with a coverage of ∼20% of the surface were distributed on a Si wafer surface and studied both before and after being annealed (at 100 and 300 °C). The two types of samples were analyzed using secondary ion mass spectroscopy (SIMS) with Bi 3  + clusters as the primary ions combined with surface etching using Ar 1000  + clusters. We observed a substantial difference in the SIMS spectra combined with a relatively short sputtering time of Ar 1000  + . In the nonannealed samples, bare Au cluster cations and Si + were observed in the SIMS spectra; AuSi + clusters were also observed in the annealed samples. These results indicate Au-silicide formation at a part of the periphery of the Au nanoparticles upon annealing. We suggest that SIMS experiments using cluster ions such as Bi 3  + can not only be used for surface elemental analyses but also provide information on local chemical environments of elements on the surface. This is an important issue in heterogeneous catalysis (e.g., strong metal-support interactions). We also advise that one should be careful interpreting the SIMS data combined with a longer Ar 1000  + sputtering time because this can deteriorate the surfaces from their original structures.

acs omega

TOF-SIMS Analysis Using Bi3+ as Primary Ions on Au Nanoparticles Supported by SiO2/Si: Providing Insight into Metal–Support Interactions