English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

The intermetallic Ti-43Al-2Cr-2Nb (at.%) alloy was directionally solidified in an electromagnetic cold crucible with different withdrawal rates (V) ranging from 0.2 to 1.0 mm昺in-1, at a constant temperature gradients (G=18 K昺m-1) . Macrostructures of the alloy were observed by optical microscopy. Microstructures of the alloy were characterized by scanning electron microscopy (SEM) in back-scattered electron mode and transmission electron microscopy. Results showed that morphologies of macrostructure depend greatly on the applied withdrawal rate. Continuous columnar grains can be obtained under slow withdrawal rates ranging from 0.2 to 0.6 mm昺in-1. The microstructure of the alloy was composed of ?/?lamellar structures and a small number of mixtures of B2 phases and blocky ?phases. The columnar grain size (d) and interlamellar spacing (? decrease with an increasing withdrawal rate. The effect of withdrawal rate on microhardness was also investigated. The microhardness of the directionally solidified Ti-43Al-2Cr-2Nb alloy increases with an increase in withdrawal rate. This is mainly attributed to the increase of B2 and ? phases as well as the refinement of lamellae

china foundry/china foundry

Dependency of microstructure and microhardness on withdrawal rate of Ti-43Al-2Cr-2Nb alloy prepared by electromagnetic cold crucible directional solidification