English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

To achieve a better material for uncooled infrared (IR) detector, polycrystalline VO2(B) thin films with layered W-doping were fabricated on Si substrates by magnetron sputtering, and the best temperature coefficient of resistance (TCR) value reached −4.1%/K. The film synthesis was in a two-step route, first deposition at room temperature and then post-deposition annealing at 450 °C, to better control the crystallization behavior. Various transmission electron microscopy (TEM) methods were employed to investigate three sets of multi-layered films with different deposition time, 10, 20, and 30 min, with especial emphasis on the effect of layered W-doping scheme on the formation of multiple VO2(B) layers. Spatial-resolved energy dispersive X-ray spectroscopy (EDS) revealed the alternative patterns of W-rich layers and W-poor layers, while the thinner films exhibited better crystallinity and texturing. By comparison with an as-deposited film, it was found that the inter-diffusion between the two types of layers was completed in the deposition step while both remained in amorphous structure. A stable W solution of about 8 cat% in VO2(B) layers measured from all these films indicated that the layered doping can tailor the multi-layered microstructure to optimize the performance of VO2(B) films.

Crystallization and inter-diffusional behaviors in the formation of VO2(B) thin film with layered W-doping