English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

A premature corrosion failure in seam-welded galvanized steel cold water pipes was reported to occur after just 18–24 months in service. The aim of the present work was to investigate the causes of this premature corrosion of pipes, through metallographic investigations. This work comprised chemical analyses, visual examination of internal surfaces of pipes and microstructural examinations of the corrosion perforation regions (pitting corrosion areas) using optical and scanning electron microscopy with energy-dispersive x-ray analysis. The investigations showed that failures resulted from incorrect installation—pipes were installed with yellow brass ball valves. When mixed with yellow brass, galvanized steel triggers dezincification and results in electrolytic action when combined with nonferrous metals, such as copper and brass.

Metallographic Investigations of the Premature Corrosion Failure of Steel Seam-Welded Galvanized Cold Water Pipes