English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Al-rich 94Al–6Mn and 94Al–4Mn–2Fe alloys were suction-cast to evaluate the feasibility of obtaining bulk quasicrystal-strengthened Al-alloys at intermediate cooling rates alloyed with non-toxic, easily accessible and affordable additions. The influence of different cooling rates on the potential formation of a quasicrystalline phase was examined by means of scanning and transmission electron microscopy, X-ray diffraction and differential scanning calorimetry. Increased cooling rates in the thinnest castings entailed a change in sample phase composition. The highest cooling rates turned out to be insufficient to form an icosahedral quasicrystalline phase (I-phase) in the binary alloy. Instead, an orthorhombic approximant phase occurred (L-phase). The addition of Fe to the 94Al–6Mn binary alloy enhanced the formation of a quasicrystalline phase. At intermediate cooling rates of 102–103 K/s, various metastable phases were formed, including decagonal and icosahedral quasicrystals and their approximants. Rods (1 mm in diameter) composed of I-phase particles embedded in Al matrix exhibited a hardness of 1.5 GPa, much higher than the 1.1 GPa of 94Al–6Mn.

Formation of a quasicrystalline phase in Al–Mn base alloys cast at intermediate cooling rates