Open AccessВПЛИВ МЕХАНІЧНОЇ АКТИВАЦІЇ НА РОЗМІРНІ ХАРАКТЕРИСТИКИ ТА ФОРМУ ЧАСТИНОК ГЛИНОПОРОШКІВ РІЗНОГО ТИПУ
Author(s) -
Yurii Budash,
Н. В. Тарасенко,
Viktoriia Plavan,
MYKOLA ZATOLOKIN,
TATIANA SHYLINTSEVA
Publication year - 2022
Publication title -
tehnologìï ta ìnžinìring
Language(s) - English
Resource type - Journals
eISSN - 2786-538X
pISSN - 2786-5371
DOI - 10.30857/2786-5371.2021.4.6
Subject(s) - montmorillonite , materials science , palygorskite , particle (ecology) , mineralogy , particle size , microanalysis , particle size distribution , composite material , clay minerals , chemistry , geology , oceanography , organic chemistry
Purpose. Determination of the influence of the process of preliminary mechanical activation on the dimensional characteristics and shape of particles of different types of clay powders.Methodology. Clay powders of montmorillonite and palygorskite type were chosen as the objects of research in this work. The process of mechanical activation of clay powders was carried out using a laboratory ball mill. For microanalysis of sample particles, the method of optical polarizing microscopy was used. Morphometric analysis of clay powder particles was performed by image analysis using the ImageJ software. At the same time, the area and perimeter were determined, and the equivalent diameter and also the shape index of the particles of the samples were calculated. The experimental data were statistically processed using the Statistica and Excel software packages.Results. The paper investigates the effect of the process of mechanical activation on the dimensional characteristics and shape of particles of montmorillonite and palygorskite type clay powders. It was found that the decrease in the average values of the equivalent particle diameter in the process of mechanical action (~14–15%) is realized mainly due to the destruction of their largest aggregates. Moreover, the intensity of this process is noticeably higher for clay of the montmorillonite type. It is shown that for both studied samples, the process of mechanical activation leads to an increase in the average values of the particle shape index (~ by 9–10%) and an increase in the uniformity of their distribution by this index.Scientific novelty. Using a detailed morphometric analysis of particles of various types of clay powders, the regularities of the influence of the mechanical activation process on the quantitative statistical characteristics of their distribution over the equivalent diameter and shape index have been established.Practical value. The results obtained will make it possible to reasonably approach the choice of pretreatment methods for clay powders intended for the production of polymer filled nanocomposite materials.