Author(s) -
Marcelo Giannini,
Andreia Assis Carvalho,
Ariovaldo Stefani,
Wladimir Franco de Sá Barbosa,
Lawrence Gonzaga Lopes
Publication year - 2017
Publication title -
brazilian journal of oral sciences/brazilian journal of oral sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.125
H-Index - 11
eISSN - 1677-3225
pISSN - 1677-3217
DOI - 10.20396/bjos.v15i4.8650036
Subject(s) - dentin , materials science , cementation (geology) , composite material , universal testing machine , bond strength , adhesive , enamel paint , dentistry , cement , curing (chemistry) , significant difference , ultimate tensile strength , mathematics , statistics , medicine , layer (electronics)
Self-adhesive, dual-polymerizing resin cements require no treatment to the prepared tooth surfaces before cementation. Aim: The aim of this study was to evaluate the influence of curing mode on bond strength (BS) of three cementing systems to bovine dentin. Methods: The buccal enamel surfaces of 50 bovine incisors were removed to expose dentin and to flat the surface. The teeth were divided into five groups (n=10), which consisted of two resin cements (Multilink and Clearfil SA Cement) that were tested in dual- (halogen light for 40 s) and self-cured modes, and a control (RelyX ARC). Two cylinders of resin cements (1.0 mm X 0.75 mm) were prepared on each bonded dentin surface. After 24h at 37oC, resin cylinders were subjected to micro-shear testing in a universal testing machine (4411/Instron - 0.5 mm/min). Data were statistically analyzed by two-way ANOVA, Tukey and Dunnett`s test (5%). Results: Multilink showed higher BS than those observed on Clearfil SA. Light-curing resulted in higher BS for both Multilink and Clearfil SA. When Multilink was light-cured, no significant difference on BS was demonstrated between it and RelyX ARC. Conclusions: The highest BS values were obtained in control group and light-cured Multilink resin cement.