Orientation relationship of eutectoid FeAl and FeAl 2
Author(s) -
Scherf A.,
Kauffmann A.,
Kauffmann-Weiss S.,
Scherer T.,
Li X.,
Stein F.,
Heilmaier M.
Publication year - 2016
Publication title -
journal of applied crystallography
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.429
H-Index - 162
ISSN - 1600-5767
DOI - 10.1107/s1600576716000911
Subject(s) - feal , lamellar structure , materials science , eutectic system , crystallography , texture (cosmology) , orientation (vector space) , microstructure , intermetallic , metallurgy , geometry , chemistry , mathematics , alloy , computer science , image (mathematics) , artificial intelligence
Fe–Al alloys in the aluminium range of 55–65 at.% exhibit a lamellar microstructure of B2‐ordered FeAl and triclinic FeAl 2 , which is caused by a eutectoid decomposition of the high‐temperature Fe 5 Al 8 phase, the so‐called ϵ phase. The orientation relationship of FeAl and FeAl 2 has previously been studied by Bastin et al. [ J. Cryst. Growth (1978), 43 , 745] and Hirata et al. [ Philos. Mag. Lett. (2008), 88 , 491]. Since both results are based on different crystallographic data regarding FeAl 2 , the data are re‐evaluated with respect to a recent re‐determination of the FeAl 2 phase provided by Chumak et al. [ Acta Cryst. (2010), C 66 , i87]. It is found that both orientation relationships match subsequent to a rotation operation of 180° about a ⟨112⟩ crystallographic axis of FeAl or by applying the inversion symmetry of the FeAl 2 crystal structure as suggested by the Chumak data set. Experimental evidence for the validity of the previously determined orientation relationships was found in as‐cast fully lamellar material (random texture) as well as directionally solidified material (∼⟨110⟩ FeAl || solidification direction) by means of orientation imaging microscopy and global texture measurements. In addition, a preferential interface between FeAl and FeAl 2 was identified by means of trace analyses using cross sectioning with a focused ion beam. On the basis of these habit planes the orientation relationship between the two phases can be described by (01) FeAl || (114) and [111] FeAl || [10]. There is no evidence for twinning within FeAl lamellae or alternating orientations of FeAl lamellae. Based on the determined orientation and interface data, an atomistic model of the structure relationship of Fe 5 Al 8 , FeAl and FeAl 2 in the vicinity of the eutectoid decomposition is derived. This model is analysed with respect to the strain which has to be accommodated at the interface of FeAl and FeAl 2 .